Comportement et rupture de fibres cellulosiques lors de leur compoundage avec une matrice polymère (Record no. 163834)

003 - Identifiant pérenne de la notice
Identifiant pérenne de la notice http://www.sudoc.fr/177885904
005 - numéro d'identification de la version
identification de la version 20190527220858.0
009 - PPN
PPN 177885904
033 ## -
-- http://www.theses.fr/2013ENMP0076
035 ## -
-- STAR43963
035 ## -
-- STAR43963
035 ## -
-- STAR43963
099 ## - Informations locales
date creation notice (koha) 2014-04-24
date modification notice (koha) 2019-05-27
100 ## - données générales de traitement
données générales de traitement 20140423d2013 k y0frey50 ba
135 ## -
-- dr|||||||||||
181 ## - Forme du contenu
Données de lien entre zones z01
Source du code non-ISO rdacontent
181 #1 - Forme du contenu
Données de lien entre zones z01
Code de la forme de contenu en ISBD
Code du qualificatif de contenu en ISBD xxxe##
182 ## - Type de médiation
Données de lien entre zones z01
Source du code non-ISO rdamedia
182 #1 - Type de médiation
Données de lien entre zones z01
Code du Type de médiation en ISBD Electronique
183 #1 - Type de support matériel
données de lien entre zones z01
source du code rdacarrier
200 1# - titre
Titre propre Comportement et rupture de fibres cellulosiques lors de leur compoundage avec une matrice polymère
Auteur principal Anne Le Duc
Auteur(s) secondaire(s) sous la direction de Tatiana Budtova
210 #1 - éditeur
Date de publication 2013
230 ## -
-- Données textuelles
304 ## - Note sur le titre et la mention de responsabilité
texte de la note Titre provenant de l'écran-titre
328 #0 - note
Détails sur la thèse ou le mémoire dont le type de diplôme Thèse de doctorat
Discipline Sciences et génie des matériaux
Organisme délivrant le diplôme Paris, ENMP
Date du diplôme 2013
330 ## - résumé
texte de la note L'objectif de ce travail de thèse, réalisé dans le cadre de la Chaire Industrielle Bioplastiques financée par Mines ParisTech et Arkema, l'Oreal, Nestle, PSA et Schneider Electric, est de fournir une étude systématique sur les relations entre les conditions opératoires du procédé de compoundage et la structure de biocomposites polypropylène/fibres lin et Tencel®. En particulier, le comportement et la rupture des fibres ont été étudiés de manière détaillée pendant la mise en œuvre à l'état fondu en mélangeur interne et par extrusion bivis.Les fibres ont été observées in-situ en écoulement dans la matrice grâce à un système rhéo-optique. Ainsi, il a été montré que la décohésion des faisceaux de lin est facilitée par un rapport de forme initial plus grand. La fragmentation des fibres résulte d'un phénomène de fatigue et est provoquée par l'accumulation des déformations et de l'énergie mécanique. Au niveau de leur point de rupture, les fibres de lin et de Tencel® se déchirent et fibrillent, alors que les fibres élémentaires de lin cassent près de leurs « genoux ». Des analyses de distributions de tailles des fibres après compoundage avec la matrice ont corroboré les observations rhéo-optiques. Lorsque les conditions de mélange sont sévères, chaque « genou » devient un point de rupture et la longueur finale des fibres de lin se retrouve être égale à la longueur moyenne entre les « genoux ». Les faisceaux de lin initialement plus courts ne se dissocient et ne se fragmentent que très peu. La rupture des fibres de lin est différente en fonction de leur taille initiale et ces fibres ne conduisent pas au même comportement rhéologique pour les composites. En revanche, pour les fibres unitaires Tencel®, la taille initiale n'a que très peu d'influence sur leurs dimensions finales, à condition que les fibres ne soient pas trop longues et trop difficiles à disperser. Le temps de mélange est apparu déterminant pour préserver le rapport de forme des fibres. La déformation cumulée s'est révélée être un meilleur paramètre que l'énergie mécanique spécifique pour décrire à la fois la rupture des fibres de lin et de Tencel®. Les propriétés mécaniques en traction uniaxiale ont enfin été caractérisées et mises en relation avec les conditions de mélange et les dimensions finales des fibres.
330 ## - résumé
texte de la note The objective of this work, performed in the frame of the Industrial Chair in Bioplastics, financed by Mines ParisTech and Arkema, l'Oreal, Nestle, PSA and Schneider Electric, is to provide a systematic study of the relationships between the compounding conditions and the structure of biocomposites based on polypropylene/ flax and Tencel® fibres. In particular, the behaviour and the rupture of fibres were studied in detail during melt processing in an internal mixer and a twin screw extruder.The fibres were observed in situ during shear flow in a matrix by rheo-optics. The decohesion of flax bundles was shown to be made easier for fibres with higher initial aspect ratio. The fibres fragmentation occured by fatigue and is caused by an accumulation of strain and mechanical energy. At the breaking point, flax and Tencel® fibres are tearing and fibrillating, whereas elementary flax fibres break at “kink bands”. The analysis of fibres size distributions after compounding has corroborated rheo-optical observations. When processing conditions are severe, each “kink band” becomes a breaking point, and the final fibres length is equal to the mean length between two “kind bands”. The short flax bundles dissociate and break up less after compounding as compared to long bundles. As a result, the rheological properties of composites are different. The initial size of Tencel® fibres has almost no effect on fibre final dimensions, provided that they are not too long and thus do not make agglomerates. The mixing time seems to be decisive to preserve fibres aspect ratio. The cumulative strain was shown to be a better parameter than specific mechanical energy to describe fibres rupture for both Tencel® and flax fibres. Uniaxial tensile properties were characterized and correlated to the processing conditions and to final dimensions of fibres.
337 ## - configuration requise
texte de la note Configuration requise : un logiciel capable de lire un fichier au format : PDF
541 ## - titre traduit ajouté par le catalogueur
titre traduit Behaviour and rupture of cellulosic fibres during their compounding with a polymer matrix
langue du titre traduit eng
606 ## - Mot Matière
Numéro de notice d'autorité 034232346
Element d'entrée Fibres cellulosiques
Numéro de notice d'autorité 029208971
Subdivision de sujet Propriétés mécaniques
Numéro de notice d'autorité 027253139
Subdivision de sujet Thèses et écrits académiques
Code du système d'indexation rameau
606 ## - Mot Matière
Numéro de notice d'autorité 033664528
Element d'entrée Composites
Subdivision de sujet Fatigue
Numéro de notice d'autorité 027253139
Subdivision de sujet Thèses et écrits académiques
Code du système d'indexation rameau
700 #1 - auteur
numéro de la notice d'autorité 177884894
Nom de l'auteur Le Duc
Prénom Anne
dates 1984-...
702 #1 - nom de personne - mention de responsabilité secondaire
numéro de la notice d'autorité 117035904
élément d'entrée Budtova
partie du nom autre que l'élément d'entrée Tatiana
dates 1963-...
code de fonction Directeur de thèse
-- Membre du jury
712 02 - collectivité - mention de responsabilité secondaire
Numéro de la notice autorité 026375249
Elément d'entrée École nationale supérieure des mines
Elément ajouté au nom ou qualificatif Paris
Code de fonction Organisme de soutenance
712 02 - collectivité - mention de responsabilité secondaire
Numéro de la notice autorité 059552867
Elément d'entrée École doctorale Sciences fondamentales et appliquées
Elément ajouté au nom ou qualificatif Nice
Code de fonction Ecole doctorale associée à la thèse
712 02 - collectivité - mention de responsabilité secondaire
Numéro de la notice autorité 026523574
Elément d'entrée Centre de mise en forme des matériaux
Elément ajouté au nom ou qualificatif Sophia Antipolis, Alpes-Maritimes
Code de fonction Laboratoire associé à la thèse
801 #3 - source de catalogage
Date de la transaction 20170628
856 4# - accès
-- PDF
-- 14436945
Version en ligne <a href="http://www.theses.fr/2013ENMP0076/document">http://www.theses.fr/2013ENMP0076/document</a>
-- Accès au texte intégral
856 4# - accès
Version en ligne <a href="http://www.theses.fr/2013ENMP0076/abes">http://www.theses.fr/2013ENMP0076/abes</a>
856 4# - accès
Version en ligne <a href="https://pastel.archives-ouvertes.fr/pastel-00982245">https://pastel.archives-ouvertes.fr/pastel-00982245</a>
930 ## -
-- 751069904:585368678
-- 751069904
-- g
991 ## -
-- 751069904:585368678
-- exemplaire créé automatiquement par STAR
Holdings
Perdu Origine geographique du document Localisation cote Statut de l'exemplaire note sur l'exemplaire
Présent En ligne En ligne https://pastel.archives-ouvertes.fr/pastel-00982245 En ligne Thèse en ligne

Powered by Koha